Digital ABS

Simulate standard ABS plastics by combining high-temperature resistance with toughness.

Digital ABS (fabricated inside the 3D printer from RGD515 and RGD535/531) is designed to simulate standard ABS plastics by combining high-temperature resistance with toughness. Digital ABS2 delivers those properties plus superior rigidity and toughness in walls thinner than 1.2 mm. Both materials are suitable for parts that require PolyJet technology’s highest possible impact resistance and shock absorption.

A wide range of applications include functional prototypes, manufacturing tools, moulds including injection moulds, snap-fit parts for high or low temperature use, casings, engine parts and covers.

Digital ABS data sheet

Digital ABS, Green

Edit
  ASTM UNITS METRIC UNITS IMPERIAL
Tensile strength D-638-03 MPa 55-60 psi 8000-8700
Elongation at break D-638-05 % 25-40 % 25-40
Modulus of elasticity D-638-04 MPa 2600-3000 psi 375,000-435,000
Flexural Strength D-790-03 MPa 65-75 psi 9,500-11,000
Flexural Modulus D-790-04 MPa 1700-2200 psi 245,000-320,000
HDT, °C @ 0.45MPa D-648-06 °C 58-68 °F 136-154
HDT, °C @ 0.45MPa after thermal post treatment procedure A D-648-06 °C 82-90 °F 180-194
HDT, °C @ 0.45MPa after thermal post treatment procedure B D-648-06 °C 92-95 °F 198-203
HDT, °C @ 1.82MPa D-648-07 °C 51-55 °F 124-131
Izod Notched Impact D-256-06 J/m 65-80 ft lb/inch 1.22-1.50
Tg DMA, Eé °C 47-53 °F 117-127
Shore Hardness (D) Scale D Scale D 85-87 Scale D 85-87
Rockwell Hardness Scale M Scale M 67-69 Scale M 67-69
Polymerized density ASTM D792 g/cm3 1.17-1.18

High Temperature Material (RGD525)

Edit
  ASTM UNITS METRIC UNITS IMPERIAL
Tensile strength D-638-03 MPa 70-80 psi 10,000-11,500
Elongation at break D-638-05 % Oct-15 % 10-15.
Modulus of elasticity D-638-04 MPa 3200-3500 psi 465,000-510,000
Flexural Strength D-790-03 MPa 110-130 psi 16,000-19,000
Flexural Modulus D-790-04 MPa 3100-3500 psi 450,000-510,000
HDT, °C @ 0.45MPa D-648-06 °C 63-67 °F 145-163
HDT, °C @ 0.45MPa after thermal post treatment procedure A D-648-06 °C 75-80 °F 167-176
HDT, °C @ 1.82MPa D-648-07 °C 55-57 °F 131-135
Izod Notched Impact D-256-06 J/m 14-16 ft lb/inch 0.262-0.300
Water Absorption, % D-570-98 24hr % 1.2-1.4 % 1.2-1.4
Tg DMA, E» °C 62-65 °F 144-149
Shore Hardness D Scale D Scale D 87-88 Scale D 87-88
Rockwell Hardness Scale M Scale M 78-83 Scale M 78-83
Polymerized density ASTM D792 g/cm3 1.17-1.18
Ash content USP281 % 0.38-0.42 % 0.38-0.42